reminder that there are good Pb-free solders (e.g. Sn99-Ag0.3-Cu0.7 with 2% RMA) that are just as fit for purpose as Pb60-Sn40, and you can switch to Pb-free without compromising how your joints flow

i used to be a PbSn die-hard but this particular alloy is just... fine? i don't have anything to complain about